Mg-Al-based hydrotalcite-type particles, chlorine-containing resin composition and process for producing the particles

ABSTRACT

A chlorine-containing resin composition for covering an electric wire of the present invention, has a heat stability of not less than 240 minutes and a volume resistivity of 5.0×10 13  to 1.0×10 16  Ω·cm when measured according to JIS K6723, and comprises:
         100 parts by weight of a chlorine-containing resin, and
 
1.5 to 10 parts by weight of Mg—Al-based hydrotalcite-type particles having a composition represented by the formula:
 
[Mg x Ca y ].Al z .(OH) 2 .A n−   p .mH 2 O
 
wherein 0.2≦z/(x+z)≦0.6; 0.01≦y/(x+z)≦0.20; x+y+z=1;
   p=(2(x+y−1)+3z)/n; A is a n-valent anion; and m is more than 0 and not more than 0.75, having a plate surface diameter of 0.1 to 1.0 μm and a thickness of 0.02 to 0.08 μm, and containing calcium at a molar ratio of Ca to a sum of Mg and Al of 0.01:1 to 0.20:1, and having a heat-resisting time of not less than 4 hours upon a chlorine-containing resin composition containing the Mg—Al-based hydrotalcite-type particles.

CROSS REFERENCE TO RELATED APPLICATION

This application is a divisional of application Ser. No. 10/302,837filed Nov. 25, 2002, now allowed, which in turn is a divisional of U.S.Pat. No. 6,509,405 B 1.

BACKGROUND OF THE INVENTION

The present invention relates to a chlorine-containing resin compositioncontaining Mg—Al-based hydrotalcite-type particles, the Mg—Al-basedhydrotalcite-type particles, and a process for producing the Mg—Al-basedhydrotalcite-type particles. More particularly, the present inventionrelates to a chlorine-containing resin composition containingMg—Al-based hydrotalcite-type particles having a large plate surfacediameter and an adequate thickness, which is not only excellent in heatstability and heat discoloration resistance but also is improved inelectrical insulating property; the Mg—Al-based hydrotalcite-typeparticles which are suitable as a stabilizer for chlorine-containingresins; and a process for producing such Mg—Al-based hydrotalcite-typeparticles.

As layered compounds, there are known various compounds as well as clayminerals or the like. Among these layered compounds, layered doublehydroxides such as hydrotalcite have such a structure capable ofinserting various anions or molecules into spacings between respectivelayers thereof and, therefore, can exhibit an anion-exchanging property.

In general, as described in Journal of the Chemical Society of Japan,1995, No. 8, pp. 622 to 628, the hydrotalcite is represented by theformula:[M²⁺ _(1−x)M³⁺ _(x)(OH)₂]_(x) ⁺[An⁻ _(x/n).yH₂O]_(x) ⁻wherein M²⁺ is a divalent metal ion such as Mg²⁺, Co²⁺, Ni²⁺ or Zn²⁺;M³⁺ is a trivalent metal ion such as Al³⁺, Fe³⁺ or Cr³⁺; An⁻ is ann-valent anion such as OH⁻, Cl⁻, CO₃ ²⁻ or SO₄ ²⁻; and x is usually 0.2to 0.33, and such hydrotalcite has a laminated crystal structure whichcomprises two-dimensional main layers composed of regular octahedralbrucite units each having a positive charge, and interlayers each havinga negative charge.

The hydrotalcite has been used in various applications because of goodanion-exchanging property thereof, for example, as ion exchangematerials, adsorbents, deodorants or the like. Also, the hydrotalcitehas been used in various other applications such as stabilizers forresins or rubbers, e.g., polyethylene, polypropylene andchlorine-containing resins (typically, vinyl chloride resins), as wellas paints, various catalysts, agricultural films, inks or the like.

In recent years, as to catalysts or the like, it has been required touse those containing no harmful metals from the standpoint ofenvironmental protection. The hydrotalcite-type particles have beenexpected to satisfy these requirements because the hydrotalcite-typeparticles have almost no toxicity and exhibit an excellent catalyticproperty or the like.

In particular, among these hydrotalcite-type particles, Mg—Al-basedhydrotalcite-type particles containing Mg²⁺ as a divalent metal ion andAl³⁺ as a trivalent metal ion, are most noticeable owing to its goodstability.

As the general production method of hydrotalcite, there is known amethod of mixing an aqueous metal salt solution containing divalentmetal ions and trivalent metal ions which constitute main layersthereof, with an aqueous carbonate solution containing carbonate ionswhich constitute interlayers thereof, and then subjecting the obtainedmixture to coprecipitation reaction while controlling the temperature,the pH value and the like. In addition to the above method of conductingthe reaction under ordinary pressure, there is also known a method ofproducing hydrotalcite under pressure by hydrothermal reaction using anautoclave.

Hitherto, hydrotalcite-type particles used for kneading into resins,have been required to possess a large plate surface diameter and anadequate thickness in the consideration of dispersibility in resins uponkneading. However, in order to obtain such hydrotalcite-type particleshaving a large plate surface diameter, it is necessary to use specificreaction conditions such as those for hydrothermal synthesis or thelike.

Further, in the case where the hydrotalcite-type particles are used as astabilizer for chlorine-containing resins or rubbers such as vinylchloride resins or the like, it is also required that the particles aresufficiently dispersed in the resins or rubbers and have a high chlorineion-capturing ability in order to obtain resin or rubber products havingan excellent heat resistance.

More particularity, among the above-described various applications, theuse of hydrotalcite-type particles as a stabilizer forchlorine-containing resins is more noticeable. Such chlorine-containingresins have been used in various applications because of good physicaland chemical properties thereof. Especially, the chlorine-containingresins are more excellent in electrical insulating property, arcresistance, tracking resistance and voltage resistance as compared topolyolefins and, therefore, have been widely used as an electricwire-covering material.

However, the chlorine-containing resins are susceptible to heatdeterioration and oxidation degradation and, therefore, suffer fromdeteriorated properties such as low elongation when used for a longperiod of time, thereby causing such a problem that the resins are nolonger usable as an electric wire-covering material.

For this reason, as the stabilizer for chlorine-containing resins as anelectric wire-covering material, there have been frequently usedlead-based compounds such as tribasic lead sulfate, lead stearate or thelike. However, it has been recently required to use those materialscontaining no toxic metal from the standpoint of environmentalprotection. Therefore, the use of hydrotalcite-type particles havingsubstantially no toxicity and an excellent function as a stabilizer forchlorine-containing resins, has been proposed (Japanese PatentApplication Laid-Open (KOKAI) Nos. 55-80445, 57-80444, 57-147552,58-122951 and 8-73687 (1996)).

More specifically, in Japanese Patent Application Laid-Open (KOKAI) No.8-73687(1996), it has been described that a halogen-containing resincomposition comprising a halogen-containing resin, specific antioxdants,hydrotalcites and zinc compounds. The hydrotalcites used in JapanesePatent Application Laid-Open (KOKAI) No. 8-73687(1996), is representedby the formula:Mg_(x).Al₂(OH)_(2x+4)CO₃.nH₂O

wherein 4≦x≦6, 0≦n≦20. Further, as the hydrotalcites used in Examples ofJapanese Patent Application Laid-Open (KOKAI) No. 8-73687(1996), thereis cited Mg_(4.5).Al₂(OH)₁₃CO₃.3.5H₂O and Mg₄.Al₂(OH)₁₂CO₃.3H₂O.

The chlorine-containing resin compositions used as an electricwire-covering material have been required to possess an excellent heatstability and a high electrical insulating property. Further, thoseresin compositions used as white- or light-colored electricwire-covering materials have been required to be free from heatdiscoloration upon processing, i.e., to show a good heat discolorationresistance. Further, in order to obtain chlorine-containing resincompositions capable of satisfying the above requirements, it isnecessary that hydrotalcite-type particles used as a stabilizer have notonly a large plate surface diameter and an adequate thickness but also ahigh chlorine ion-capturing ability.

At the present time, it has been strongly demanded to provideMg—Al-based hydrotalcite-type particles which have a large plate surfacediameter and an adequate thickness, and is suitable as a stabilizer forchlorine-containing resins. However, such Mg—Al-based hydrotalcite-typeparticles capable of satisfying the above properties have not beenobtained yet.

In the conventional coprecipitation methods, it is not possible toobtain hydrotalcite-type particles having a large plate surfacediameter. Under specific reaction conditions such as those ofhydrothermal synthesis, although hydrotalcite-type particles having alarge plate surface diameter can be produced, when suchhydrotalcite-type particles are used as a stabilizer ofchlorine-containing resins, a sufficient heat resistance can not beobtained.

Especially, it has been strongly demanded to provide achlorine-containing resin composition which is excellent in heatstability and heat discoloration resistance and is improved inelectrical insulating property. However, such a chlorine-containingresin composition capable of satisfying these requirements have not beenobtained yet.

Thus, such conventional techniques described in the above priorpublications, have failed to provide a sufficient stabilizing effectand, therefore, the heat stability, heat discoloration resistance andelectrical insulating property of the conventional chlorine-containingresin compositions are insufficient.

As a result of the present inventors' earnest studies, it has been foundthat when by kneading in a chlorine-containing resin Mg—Al-basedhydrotalcite-type particles having a plate surface diameter of 0.1 to1.0 μm and a thickness of 0.02 to 0.08 μm, obtained by mixing an aqueousanion-containing alkali solution, an aqueous magnesium salt solution andan aqueous aluminum salt solution with each other, adding an aqueouscalcium salt solution to the mixed solution such that the molar ratio ofCa to a sum of Mg and Al is 0.01:1 to 0.2:1, and aging the obtainedsolution at a temperature of 60 to 105° C. while controlling the pHvalue of the solution to 10 to 14, the obtained resin composition isconsiderably improved in heat stability, heat discoloration resistanceand electrical insulating property. The present invention has beenattained on the basis of this finding.

SUMMARY OF THE INVENTION

It is an object of the present invention to provide achlorine-containing resin composition which is not only excellent inheat stability and heat discoloration resistance but also shows a highelectrical insulating property.

It is another object of the present invention to provide Mg—Al-basedhydrotalcite-type particles which have a large plate surface diameterand an adequate thickness, and are suitable as a stabilizer forchlorine-containing resins or the like.

To accomplish the aim, in a first aspect of the present invention, thereis provided a chlorine-containing resin composition for covering anelectric wire, having a heat stability of not less than 240 minutes anda volume resistivity of 5.0×10¹³ to 1.0×10¹⁶ Ω·cm when measuredaccording to JIS K6723, and comprising:

100 parts by weight of a chlorine-containing resin, and

1.5 to 10 parts by weight of Mg—Al-based hydrotalcite-type particleshaving a composition represented by the formula:[Mg_(x)Ca_(y)].Al_(z).(OH)₂.A^(n−) _(p). mH₂Owherein 0.2≦z/(x+z)≦0.6; 0.01≦y/(x+z)≦0.20; x+y+z=1; p=(2(x+y−1)+3z)/n;A is a n-valent anion; and m is more than 0 and not more than 0.75,having a plate surface diameter of 0.1 to 1.0 μm and a thickness of 0.02to 0.08 μm, and containing calcium at a molar ratio of Ca to a sum of Mgand Al of 0.01:1 to 0.20:1, and having a heat-resisting time of not lessthan 4 hours when measured by the following methods (1) to (3):

(1) After the hydrotalcite-type particles together with additives aremixed in a vinyl chloride resin at the following mixing ratio, 50 g ofthe obtained mixture is kneaded at 155° C. for 3 minutes using hot rollswhose gap is set to 0.75 mm, thereby obtaining a kneaded sheet.

Composition of Mixture:

Hydrotalcite-type particles 3 parts by weight Vinyl chloride resin(degree 100 parts by weight of polymerization: 1,300, tradename:TK-1,300, produced by Shin-Etsu Kagaku Kogyo Co., Ltd.) Diethylhexylphthalate (DOP, 50 parts by weight produced by Dai-Hachi Kagaku Co.,Ltd.) Calcium stearate 2 parts by weight Zinc stearate 0.4 part byweight 1,3-diphenyl-1,3-propane-dione 0.2 part by weight Diethylphosphite 0.5 part by weight

(2) The obtained kneaded sheet is pressure-treated using a hot press,thereby producing a sheet piece having a thickness of 1.5 mm. The pressconditions are as follows:

press temperature: 160° C.; press pressure: 100 kg/cm²;

press time: 1 minute; press gap: 1.5 mm; and

amount treated: 35 g.

(3) The obtained sheet piece (20 mm×20 mm) is placed in an oven so as tobe allowed to stand in air at 180° C. The time required until the sheetpiece is black-discolored is determined as a heat-resisting time.

In a second aspect of the present invention, there is provided anelectric wire material having a heat stability of not less than 240minutes and a volume resistivity of 5.0×10¹³ to 1.0×10¹⁶ Ω·cm whenmeasured according to JIS K6723, and comprising the chlorine-containingresin composition comprising 1.5 to 10 parts by weight of Mg—Al-basedhydrotalcite-type particles having a composition represented by theformula:[Mg_(x)Ca_(y)].Al_(z). (OH)₂.A^(n−) _(p).mH₂Owherein 0.2≦z/(x+z)≦0.6; 0.01≦y/(x+z)≦0.20; x+y+z=1; p=(2(x+y−1)+3z)/n;A is a n-valent anion; and m is more than 0 and not more than 0.75,having a plate surface diameter of 0.1 to 1.0 μm and a thickness of 0.02to 0.08 μm and containing calcium at a molar ratio of Ca to a sum of Mgand Al of 0.01:1 to 0.20:1, and exhibiting a heat-resisting time of notless than 4 hours upon a chlorine-containing resin compositioncontaining the Mg—Al-based hydrotalcite-type particles; and 100 parts byweight of a chlorine-containing resin.

In a third aspect of the present invention, there are providedMg—Al-based hydrotalcite-type particles having a composition representedby the formula:[Mg_(x)Ca_(y)].Al_(z).(OH)₂.A^(n−) _(p).mH₂Owherein 0.2≦z/(x+z)≦0.6; 0.01≦y/(x+z)≦0.20; x+y+z=1; p=(2(x+y−1)+3z)/n;A is a n-valent anion; and m is more than 0 and not more than 0.75,having a plate surface diameter of 0.1 to 1.0 μm and a thickness of 0.02to 0.08 μm and containing calcium at a molar ratio of Ca to a sum of Mgand Al of 0.01:1 to 0.20:1, and having a heat-resisting time of not lessthan 4 hours when measured by the following methods (1) to (3):

(1) After the hydrotalcite-type particles together with additives aremixed in a vinyl chloride resin at the following mixing ratio, 50 g ofthe obtained mixture is kneaded at 155° C. for 3 minutes using hot rollswhose gap is set to 0.75 mm, thereby obtaining a kneaded sheet.

Composition of Mixture:

Hydrotalcite-type particles 3 parts by weight Vinyl chloride resin(degree 100 parts by weight of polymerization: 1,300, tradename:TK-1,300, produced by Shin-Etsu Kagaku Kogyo Co., Ltd.) Diethylhexylphthalate (DOP, 50 parts by weight produced by Dai-Hachi Kagaku Co.,Ltd.) Calcium stearate 2 parts by weight Zinc stearate 0.4 part byweight 1,3-diphenyl-1,3-propane-dione 0.2 part by weight Diethylphosphite 0.5 part by weight

(2) The obtained kneaded sheet is pressure-treated using a hot press,thereby producing a sheet piece having a thickness of 1.5 mm. The pressconditions are as follows:

press temperature: 160° C.; press pressure: 100 kg/cm²;

press time: 1 minute; press gap: 1.5 mm; and

amount treated: 35 g.

(3) The obtained sheet piece (20 mm×20 mm) is placed in an oven so as tobe allowed to stand in air at 180° C. The time required until the sheetpiece is black-discolored is determined as a heat-resisting time.

In a fourth aspect of the present invention, there is provided astabilizer for chlorine-containing resins, comprising Mg—Al-basedhydrotalcite-type particles having a composition represented by theformula:

 [Mg_(x)Ca_(y)].Al_(z).(OH)₂.A^(n−) _(p).mH₂O

wherein 0.2≦z/(x+z)≦0.6; 0.01≦y/(x+z)≦0.20; x+y+z=1; p=(2(x+y−1)+3z)/n;A is a n-valent anion; and m is more than 0 and not more than 0.75,having a plate surface diameter of 0.1 to 1.0 μm and a thickness of 0.02to 0.08 μm and containing calcium at a molar ratio of Ca to a sum of Mgand Al of 0.01:1 to 0.20:1, and exhibiting a heat-resisting time of notless than 4 hours upon a chlorine-containing resin compositioncontaining the Mg—Al-based hydrotalcite-type particles.

In a fifth aspect of the present invention, there is provided a processfor producing the Mg—Al-based hydrotalcite-type particles, comprising:

mixing an anion-containing alkali solution, an aqueous magnesium saltsolution and an aqueous aluminum salt solution with each other;

adding an aqueous calcium solution to the mixed solution such that themolar ratio of Ca to a sum of Mg and Al is 0.01:1 to 0.20:1; and

aging the obtained solution at a temperature of 60 to 105° C. whilecontrolling the pH value of the solution to 10 to 14.

DETAILED DESCRIPTION OF THE INVENTION

The present invention is described in detail below.

First, Mg—Al-based hydrotalcite-type particles according to the presentinvention are explained.

The Mg—Al-based hydrotalcite-type particles according to the presentinvention are of a plate-like shape, and have a plate surface diameterof usually 0.1 to 1.0 μm and a thickness of usually 0.02 to 0.08 μm.

When the plate surface diameter of the Mg—Al-based hydrotalcite-typeparticles is less than 0.1 μm, the particles are insufficient indispersibility in resins when kneaded thereinto. Also, it is difficultto industrially produce such Mg—Al-based hydrotalcite-type particleshaving the plate surface diameter is more than 1.0 μm. The plate surfacediameter of the Mg—Al-based hydrotalcite-type particles according to thepresent invention is preferably 0.2 to 0.8 μm.

When the thickness of the Mg—Al-based hydrotalcite-type particles isless than 0.02 μm, the Mg—Al-based hydrotalcite-type particles areinsufficient in dispersibility in resins when kneaded thereinto. Also,it is difficult to industrially produce such Mg—Al-basedhydrotalcite-type particles having the thickness is more than 0.08 μm.The thickness of the Mg—Al-based hydrotalcite-type particles accordingto the present invention is preferably 0.025 to 0.075 μm.

In the Mg—Al-based hydrotalcite-type particles according to the presentinvention, the molar ratio of Ca to a sum of Mg and Al is usually 0.01:1to 0.20:1, preferably 0.03:1 to 0.15:1.

When the molar ratio of Ca to a sum of Mg and Al in the Mg—Al-basedhydrotalcite-type particles is less than 0.01:1 or more than 0.20:1, itis difficult to obtain particles having a sufficiently large platesurface diameter.

When a resin sheet prepared by using a chlorine-containing resincomposition obtained by mixing 3 parts by weight of the Mg—Al-basedhydrotalcite-type particles according to the present invention with 100parts by weight of a vinyl chloride resin, is heated at 180° C., theresin sheet can withstand the heating condition for not less than 4hours (the time is hereinafter referred to as “heat-resisting time”).

When the heat-resisting time is less than 4 hours, thechlorine-containing resin composition containing the Mg—Al-basedhydrotalcite-type particles, is deteriorated. The longer theheat-resisting time, the higher the chlorine ion-capturing ability ofthe Mg—Al-based hydrotalcite-type particles, which is capable ofeffectively capturing harmful hydrogen chloride generated by the heat,light or oxygen decomposition of the chlorine-containing resin, so thatthe deterioration in quality and properties of the chlorine-containingresin is suppressed. The heat-resisting time of such a resin ispreferably not less than 5 hours. The upper limit of the heat-resistingtime of the resin is preferably 8 hours.

The Mg—Al-based hydrotalcite-type particles according to the presentinvention are represented by the following composition formula:[Mg_(x)Ca_(y)].Al_(z).(OH)₂.A^(n−) _(p).mH₂Owherein 0.2≦z/(x+z)≦0.6; 0.01≦y/(x+z)≦0.20; x+y+z=1; p=(2(x+y−1)+3z)/n;A is an n-valent anion; and m is more than 0 and not more than 0.75.

With respect to Mg and Al contents of the Mg—Al-based hydrotalcite-typeparticles according to the present invention, the ratio: z/(x+z) whereinx is Mg and z is Al, is 0.2:1 to 0.6:1. When the ratio: z/(x+z) is lessthan 0.2:1 or more than 0.6:1 (i.e., when the ratio of Mg to Al is lessthan 4:1 or more than 2:3), it may become difficult to obtainsingle-phase hydrotalcite-type particles. The ratio: z/(x+z) ispreferably in the range of 0.2:1 to 0.56:1.

The sum of x, y and z is 1 (x+y+z=1).

The anion (A^(n−)) contained in the Mg—Al-based hydrotalcite-typeparticles according to the present invention may be selected from thegroup consisting of a hydroxy ion (OH⁻), a carbonate ion (CO₃ ²⁻) and asulfate ion (SO₄ ²⁻). Among these anions, the carbonate ion ispreferred.

The plate ratio (plate surface diameter/thickness) of the Mg—Al-basedhydrotalcite-type particles according to the present invention ispreferably 2:1 to 15:1, more preferably 2:1 to 13:1, and the BETspecific surface area value thereof is preferably 8 to 90 m²/g, morepreferably 8 to 70 m²/g.

Next, the process for producing the Mg—Al-based hydrotalcite-typeparticles according to the present invention, is described.

The Mg—Al-based hydrotalcite-type particles according to the presentinvention is produced by mixing an anion-containing alkali solution, anaqueous magnesium salt solution and an aqueous aluminum salt solutionwith each other; adding an aqueous calcium solution to the mixedsolution; and aging the obtained solution at a temperature of 60 to 105°C. for 2 to 24 hours while controlling the pH value of the solution to10 to 14.

In the present invention, as the aqueous anion-containing alkalisolution, there may be suitably used a mixed alkali solution composed ofan aqueous anion-containing solution such as sodium carbonate, sodiumhydrogencarbonate, potassium carbonate, potassium hydrogencarbonate orthe like, and an aqueous alkali hydroxide solution such as sodiumhydroxide, potassium hydroxide or the like.

As the aqueous anion-containing solution, the use of an aqueous sodiumcarbonate solution is preferred.

As the aqueous alkali hydroxide solution, the use of an aqueous sodiumhydroxide solution is preferred.

In the present invention, as the aqueous magnesium salt solution, theremay be used an aqueous magnesium sulfate solution, an aqueous magnesiumchloride solution, an aqueous magnesium nitrate solution or the like.Among these aqueous magnesium salt solutions, the aqueous magnesiumsulfate solution and the aqueous magnesium chloride solution arepreferred.

In the present invention, as the aqueous aluminum salt solution, theremay be used an aqueous aluminum sulfate solution, an aqueous aluminumchloride solution, an aqueous aluminum nitrate solution or the like.Among these aqueous aluminum salt solutions, the aqueous aluminumsulfate solution and the aqueous aluminum chloride solution arepreferred.

The order of mixing or addition of the aqueous anion-containingsolution, the aqueous magnesium salt solution and the aqueous aluminumsalt solution is not particularly restricted. All of the aqueoussolutions may be mixed together at the same time. Preferably, a mixedsolution composed of the aqueous magnesium salt solution and the aqueousaluminum salt solution is added to the aqueous anion-containingsolution.

Further, the addition of each aqueous solution may be carried out byadding the whole part thereof at once, by adding the solution in two ormore separate parts or by continuously dropping the solution.

In the present invention, the aqueous calcium salt solution is added tothe mixed solution composed of the aqueous anion-containing solution,the aqueous magnesium salt solution and the aqueous aluminum saltsolution.

As the aqueous calcium salt solution, there may be used an aqueouscalcium chloride solution, an aqueous calcium nitrate solution or thelike. Among these aqueous calcium salt solutions, the use of the aqueouscalcium chloride solution is preferred.

The aqueous calcium salt solution may be added in such an amount thatthe molar ratio of Ca to a sum of Mg and Al is usually 0.01:1 to 0.20:1,preferably 0.03:1 to 0.15:1.

In the reaction solution prepared by mixing the aqueous anion-containingsolution, the aqueous magnesium salt solution, the aqueous aluminum saltsolution and the aqueous calcium salt solution together, theconcentration of the magnesium salt is preferably 0.1 to 1.5 mol/liter,more preferably 0.1 to 1.2 mol/liter; the concentration of the aluminumsalt is preferably 0.03 to 1.0 mol/liter, more preferably 0.04 to 0.8mol/liter; the concentration of the calcium salt is preferably 0.01 to0.2 mol/liter, more preferably 0.01 to 0.15 mol/liter; the concentrationof the anion is preferably 0.05 to 1.4 mol/liter, more preferably 0.06to 1.2 mol/liter; and the concentration of the alkali hydroxide ispreferably 0.5 to 8 mol/liter, more preferably 0.8 to 6 mol/liter.

In the reaction solution, the molar ratio of CO₃ to Al is preferably 0.5to 2.0, more preferably 0.5 to 1.5.

The temperature used for the aging reaction of the present invention isusually 60 to 105° C., preferably 80 to 105° C. When the agingtemperature is less than 60° C., it is difficult to produce thehydrotalcite-type particles having a large plate surface diameter. Whenthe aging temperature is more than 105° C., it is necessary to use apressure vessel such as autoclave in the aging reaction, resulting inuneconomical process.

In the present invention, during the aging reaction, the pH value of thereaction solution is adjusted to usually 10 to 14, preferably 11 to 14.When the pH value is less than 10, it is difficult to obtainhydrotalcite-type particles having a large plate surface diameter and anadequate thickness.

The aging time of the present invention is preferably 2 to 24 hours.When the aging time is less than 2 hours, it is difficult to obtainhydrotalcite-type particles having a large plate surface diameter and anadequate thickness. When the aging time is more than 24 hours, theprocess becomes uneconomical.

After completion of the aging reaction, the obtained particles arewashed with water by ordinary methods and then dried, thereby producingMg—Al-based hydrotalcite-type particles according to the presentinvention.

Next, the chlorine-containing resin composition according to the presentinvention is described.

The heat stability of the chlorine-containing resin composition isusually not less than 240 minutes, preferably not less than 350 minutes,more preferably not less than 400 minutes, still more preferably notless than 420, most preferably not less than 460 minutes when measuredaccording to JIS K6723. When the heat stability is less than 240minutes, the chlorine-containing resin composition is unsuitable forcovering electric wires. The more excellent the heat stability, the morethe chlorine-containing resin become to be hardly decomposed. The upperlimit of the heat stability of the chlorine-containing resin compositionis preferably 1,000 minutes.

As to the electrical insulating property of the chlorine-containingresin composition according to the present invention, the volumeresistivity of the resin composition is usually 5.0×10¹³ to 1.0×10¹⁶Ω·cm, preferably 8.0×10¹³ to 1.0×10¹⁴ Ω·cm when measured according toJIS K6723. When the volume resistivity is less than 5.0×10¹³ Ω·cm, thechlorine-containing resin composition is unsuitable for coveringelectric wires.

The chlorine-containing resin composition according to the presentinvention contains the above Mg—Al-based hydrotalcite-type particles of1.5 to 10 parts by weight based on 100 parts by weight of thechlorine-containing resin and a plasticizer of 30 to 90 parts by weightbased on 100 parts of the chlorine-containing resin, and may furthercontain other stabilizers and additives.

Meanwhile, as the hydrotalcite-type particles, there may be usedMg—Al-based hydrotalcite-type particles surface-coated with hydroxidesand/or oxides of silicon, rosins, organic silane compounds, higher fattyacids or the like. Such surface-coated hydrotalcite-type particles aremore improved in dispersibility in the chlorine-containing resin.

The coating amount of the hydroxides and/or oxides of silicon is usuallynot more than 50.0% by weight, preferably 0.05 to 50.0% by weight, morepreferably 0.05 to 45.0% by weight (calculated as SiO₂) based on theweight of the Mg—Al-based hydrotalcite-type particles to besurface-coated.

The coating amount of the rosins is usually not more than 25.0% byweight, preferably 0.2 to 25.0% by weight (calculated as C) based on theweight of the Mg—Al-based hydrotalcite-type particles to besurface-coated.

The coating amount of the organic silane compounds is usually not morethan 18.0% by weight, preferably 0.2 to 18.0% by weight (calculated asC) based on the weight of the Mg—Al-based hydrotalcite-type particles tobe surface-coated.

The coating amount of the higher fatty acids is usually not more than20.0% by weight, preferably 0.2 to 20.0% by weight (calculated as C)based on the weight of the Mg—Al-based hydrotalcite-type particles to besurface-coated.

As the chlorine-containing resin, there may be exemplified polyvinylchloride, copolymers containing vinyl chloride as a main component,chlorinated polyethylene, polyvinylidene chloride, chlorinatedpolypropylene, chlorinated polyvinyl chloride or mixtures thereof. Amongthem, polyvinyl chloride is preferred. The degree of polymerization ofpolyvinyl chloride is preferably 1,000 to 1,500.

When the content of the hydrotalcite-type particles is less than 1.5parts by weight based on 100 parts of the chlorine-containing resin, theparticles cannot exhibit a sufficient effect as a stabilizer. When thecontent of the hydrotalcite-type particles is more than 10 parts byweight, no further stabilizing effect is obtained since the effect isalready saturated. In addition, if a too large amount of thehydrotalcite-type particles is added, the chlorine-containing resincomposition tends to undergo foaming, thereby sometimes adverselyaffecting an electrical insulating property and other necessaryproperties thereof. The content of the hydrotalcite-type particles ispreferably 1.5 to 10 parts by weight, more preferably 1.5 to 8 parts byweight, still more preferably 1.5 to 6 parts by weight based on 100parts of the chlorine-containing resin.

As the plasticizer, trimellitic acid esters, phthalic acid esters,polyesters or the like may be exemplified.

As the trimellitic acid esters, there may be exemplifiedtrioctyltrimertate, tri-n-octyl-n-decyltrimeritate or the like.

As the phthalic acid esters, there may be exemplified diisononylphthalate, di-2-ethylhexyl phthalate, dinonyl phthalate or the like.

As the polyesters, there may be exemplified polypropylene adipate,polypropylene sebacate or the like.

When the content of the plasticizer is less than 30 parts by weightbased on 100 parts of the chlorine-containing resin, it is difficult toobtain a resin composition having a flexibility required for coveringelectric wires. When the content of the plasticizer is more than 90parts by weight, no further flexibility-imparting effect is obtainedsince the effect is already saturated.

Examples of the other stabilizers may include zinc compounds,β-diketones, phosphites, polyvalent alcohol-based compounds, higherfatty acids, epoxy-based compounds or the like. Among these stabilizers,in the consideration of synergistic effect with the hydrotalcite-typeparticles, zinc compounds are preferred. The amount of the otherstabilizers is preferably not more than 20 parts by weight based on 100parts by weight of the chlorine-containing resin.

As the zinc compounds, there may be used zinc stearate, zinc laurate,zinc ricinoleate or the like. Among them, zinc stearate is preferred.

The amount of the zinc compound added is preferably 0.2 to 2.5 parts byweight, more preferably 0.5 to 2.2 parts by weight based on 100 parts byweight of the chlorine-containing resin.

As the β-diketones, there may be exemplified dibenzoyl methane, stearoylbenzoyl methane, dehydroacetic acid or the like.

As the phosphites, there may be exemplified alkylallyl phosphites,trialkyl phosphites or the like.

As the polyvalent alcohol-based compounds, there may be exemplifieddipentaerythritol, pentaerythritol, glycerol, diglycerol, trimethylolpropane or the like.

As the higher fatty acids, there may be exemplified stearic acid, lauricacid, oleic acid or the like. Among these higher fatty acids, stearicacid is preferred.

As the epoxy-based compounds, there may be exemplified epoxidatedlinseed oil, epoxidated soybean oil or the like.

Examples of the other additives may include antioxidants, electricresistance-increasing agents, gelling accelerators, extenders, flameretardants, lubricants, mildewproofing agents or the like. The amount ofthe other additives is preferably not more than 40 parts by weight basedon 100 parts by weight of the chlorine-containing resin.

As the anitioxidants, there may be exemplified phenol-based compounds,amine-based compounds, phosphate-based compounds or the like.

As the phenol-based compounds, there may be exemplified 2,6-di-tertiarybutyl-paracresol, 2,4,6-tri-tertiary butylphenol, styrenated phenol orthe like.

As the amine-based compounds, there may be exemplifiedphenyl-β-naphthylamine, N,N′-diphenyl-p-phenylenediamine or the like.

As the phosphate-based compounds, there may be exemplified triphenylphosphite, diphenyl decyl phosphite, phenyl isodecyl phosphite or thelike.

As the electric resistance-increasing agents, there may be exemplifiedclay, mica, aluminum oxide, barium titanate or the like.

As the gelling accelerators, there may be exemplified polyesters whereinOH groups are introduced into the terminal, acrylonitrile-styrenecopolymers, methylmethacrylate-styrene copolymers or the like.

As the extenders, there may be exemplified calcium carbonate, silica,glass beads, mica, glass fibers or the like.

As the flame retardants, there may be exemplified inorganic flameretardants such as antimony trioxide, aluminum hydroxide or zinc borate,bromine-containing organic flame retardants, halogen-containingphosphate-based flame retardants or the like.

As the lubricants, there may be exemplified calcium stearate, magnesiumstearate, barium stearate or the like.

As the mildewproofing agents, there may be exemplified2,4,4′-trichloro-2′-hydroxydiphenyl-ether,N-(trichloromethyl-thio)-4-cyclohexel, 2-dicarboxiamide,2-(4-thiazolyl)-benzimidazol or the like.

If coloring of the chlorine-containing resin composition is required,the resin composition may further contain pigments.

The process for producing the chlorine-containing resin compositionaccording to the present invention is described below.

The chlorine-containing resin composition according to the presentinvention can be produced by ordinary methods. For example, in the casewhere the resin composition is produced in the form of a kneaded sheetfor covering electric wires, the chlorine-containing resin, thehydrotalcite-type particles and the above-described various stabilizersor additives are mixed with each other at a predetermined mixing ratio,and the resultant mixture is kneaded together using hot rolls at atemperature of preferably 145 to 180° C. The kneaded material is thenpressure-treated using a hot press at a temperature of preferably 150 to190° C. to obtain a sheet.

The point of the present invention is that Mg—Al-based hydrotalcite-typeparticles having a large plate surface diameter and an adequatethickness is produced under ordinary pressure by adding a specificamount of the aqueous calcium salt solution and subjecting tocoprecipitation reaction.

The reason why the Mg—Al-based hydrotalcite-type particles having alarge plate surface is obtained, is not clearly known yet. However, itis considered as follows. That is, when the aqueous calcium saltsolution is added, calcium ions having a large ion radius areincorporated into a network of Mg—Al layers (brucite layers), so thatthe distortion of the crystal structure due to aluminum having a smallion radius is eliminated, thereby accelerating the crystal growth.

The reason why the heat resistance of the chlorine-containing resin orthe like is enhanced by kneading the Mg—Al-based hydrotalcite-typeparticles according to the present invention, is considered as follows.That is, since calcium is incorporated into the brucite layers, thehydrotalcite-type particles can be further enhanced in chlorineion-capturing ability. Due to the fact that unstable chlorine ions inthe chlorine-containing resin are more effectively captured by thehydrotalcite-type particles, the resin is improved in stability and,therefore, show a higher heat resistance.

Another point of the present invention is that the chlorine-containingresin composition according to the present invention is excellent inheat stability and electric insulating property for covering electricwires.

The reason why the chlorine-containing resin composition according tothe present invention is excellent in heat stability, is considered asfollows. That is, since the Mg—Al-based hydrotalcite-type particlesaccording to the present invention has a high chlorine-capturingability, the chlorine-containing resin composition containing thehydrotalcite-type particles show a high heat stability.

Also, the Mg—Al-based hydrotalcite-type particles according to thepresent invention has the effect of preventing zinc from being burnt(zinc-burning). Therefore, it is possible to blend a large amount ofzinc compounds in the chlorine-containing resin composition. Since thezinc compounds such as zinc stearate not only effectively enhance a heatstability but also are inexpensive, it is advantageous to add a largeamount of these zinc compounds into the resin composition. In addition,the zinc compounds show a synergistic effect of improving a heatdiscoloration resistance when used together with barium salts or calciumsalts.

The reason why the chlorine-containing resin composition according tothe present invention exhibits an excellent electric insulatingproperty, is not clearly known yet. However, it is considered asfollows. That is, since the Mg—Al-based hydrotalcite-type particlesaccording to the present invention has a high anion-exchanging property,anions as decomposed products discharged from the chlorine-containingresin composition which act as carriers for electric charges, areabsorbed in the particles, thereby enhancing an electric resistance ofthe resin composition.

As described above, since the Mg—Al-based hydrotalcite-type particlesaccording to the present invention exhibit a large plate surfacediameter and an adequate thickness, when the hydrotalcite-type particlesare kneaded into a chlorine-containing resin, the obtained resincomposition shows an excellent heat resistance. Therefore, theMg—Al-based hydrotalcite-type particles according to the presentinvention are suitable as a stabilizer for chlorine-containing resins.

Further, the chlorine-containing resin composition according to thepresent invention is excellent not only in heat stability and heatdiscoloration resistance but also in electric insulating property.Therefore, the resin composition according to the present invention issuitable for covering electric wires.

EXAMPLES

The present invention is described in more detail by Examples andComparative Examples, but the Examples are only illustrative and,therefore, not intended to limit the scope of the present invention.

Various properties were evaluated by the following methods.

(1) The plate surface diameter of hydrotalcite-type particles isexpressed by the average of values measured from an electron micrograph.

(2) The thickness of hydrotalcite-type particles is expressed by thevalue calculated from the diffraction peak curve of (003) crystal planeof the hydrotalcite-type particles according to Scherrer's formula byusing an X-ray diffractometer RAD-2A (manufactured by Rigaku Denki Co.,Ltd.; type of X-ray tube: Fe, tube voltage: 40 kV; tube current: 20 mA;goniometer: wide-angle goniometer, sampling width: 0.010°, scanningspeed: 0.5°/min., light-emitting slit: 1°, scattering slit: 1°,light-receiving slit: 0.30 mm).

(3) The identification of hydrotalcite-type particles is conducted byX-ray diffraction method using the above X-ray diffractometer, and themeasurement is carried out at an diffraction angle (2θ) of 5 to 90°.

(4) The respective indices x, v and z of the composition formula:[Mg_(x)Ca_(y)].Al_(z).(OH)₂.A^(n−) _(p).mH₂O of Mg—Al-basedhydrotalcite-type particles are determined by dissolving the particlesin acid and measuring amounts of respective elements by using aninductively coupled plasma atomic emission spectroscope SPS4000(manufactured by Seiko Denshi Kogyo Co., Ltd.).

(5) The silicon content (% by weight (calculated as SiO₂)) of thehydrotalcite-type particles surface-coated with hydroxides or oxides ofsilicon, is measured by X-ray fluorescence spectroscopy.

(6) The carbon content (wt. %) when using CO₃ ²⁻ as an anion (A^(n−)) ismeasured by a Carbon-Sulfur Analyzer EMIA-2200 (manufactured by HoribaCo., Ltd.).

(7) The heat-resisting time of a vinyl chloride resin containingMg—Al-based hydrotalcite-type particles is measured by the followingmethod.

(i) After the hydrotalcite-type particles together with additives aremixed in a vinyl chloride resin at the following mixing ratio, 50 g ofthe obtained mixture is kneaded at 155° C. for 3 minutes using hot rollswhose gap is set to 0.75 mm, thereby obtaining a kneaded sheet.

Composition of Mixture:

Hydrotalcite-type particles 3 parts by weight Vinyl chloride resin(degree 100 parts by weight of polymerization: 1,300, tradename:TK-1,300, produced by Shin-Etsu Kagaku Kogyo Co., Ltd.) Diethylhexylphthalate (DOP, 50 parts by weight produced by Dai-Hachi Kagaku Co.,Ltd.) Calcium stearate (extra pure 2 parts by weight reagent) Zincstearate (extra pure reagent) 0.4 part by weight1,3-diphenyl-1,3-propane-dione 0.2 part by weight (extra pure reagent)Diethyl phosphite (extra pure 0.5 part by weight reagent)

(ii) The obtained kneaded sheet is pressure-treated using a hot press,thereby producing a sheet piece having a thickness of 1.5 mm. The pressconditions are as follows:

-   -   press temperature: 160° C.; press pressure: 100 kg/cm²;    -   press time: 1 minute; press gap: 1.5 mm; and    -   amount treated: 35 g.

(iii) The obtained sheet piece (20 mm×20 mm) is placed in an oven so asto be allowed to stand in air at 180°C., thereby conducing a heat test.The time required until the sheet piece is black-discolored isdetermined as a heat-resisting time.

(8) The heat stability of a chlorine-containing resin composition ismeasured according to JIS K6723 with respect to a 1 mm-thick sheetproduced by the above method using hot roll and hot press both heated to160° C.

(9) The electric insulating property of the chlorine-containing resincomposition is evaluated by measuring a volume resistivity of the abovesheet according to JIS K6723.

(10) The heat discoloration resistance of the chlorine-containing resincomposition is evaluated by visually observing the color tone of theabove sheet and classifying the observation results into the followingfour ranks.

-   -   A: excellent (no change of color)    -   B: good (slight change of color)    -   C: poor (change to yellowish brown color)    -   D: bad (Change to brown˜black color)

Example 1

<Production of Mg—Al-Based Hydrotalcite-Type Particles>

500 milliliters of an aqueous sodium carbonate solution having a CO₃ ²⁻ion concentration of 0.875 mol/liter was mixed with 3 liters of anaqueous sodium hydroxide solution having a NaOH concentration of 5.308mol/liter. The resultant mixed solution was stirred at 60° C. in areactor. Thereafter, the solution was added to a mixed solution of 500ml of an aqueous 3.75 mol/l magnesium sulfate solution and 500 ml of anaqueous 0.625 mol/l aluminum sulfate solution and then mixed with 200 mlof an aqueous 0.75 mol/l calcium chloride solution, thereby obtaining areaction solution having a total volume of 5 liters. The obtainedsolution in the reactor was aged at 95° C. for 18 hours while stirringand controlling the pH value to 12.5, thereby obtaining a whiteprecipitate. The obtained white precipitate was filtered out, washedwith water and then dried at 60° C. The obtained white particles wereanalyzed for identification thereof, and confirmed to behydrotalcite-type particles.

The obtained Mg—Al-based hydrotalcite-type particles had an averageplate surface diameter of 0.40 μm, a thickness of 0.0605 μm and a BETspecific surface area of 11.6 m²/g. The composition of the obtainedMg—Al-based hydrotalcite-type particles was:[Mg_(0.709)Ca_(0.055)].Al_(0.236).(OH)₂.(CO₃ ²⁻)_(0.118).0.501H₂O.

When the sheet piece prepared by using the obtained Mg—Al-basedhydrotalcite-type particles was heated at 180° C., the heat-resistingtime thereof was determined to be 6 hours.

Examples 2 to 8 and Comparative Examples 1 to 7

The same procedure as defined in Example 1 was conducted except thatkind and concentration of magnesium compound, kind and concentration ofaluminum compound, concentration of sodium carbonate, concentration ofaqueous alkali solution, amount and concentration of calcium salt added,time of addition of calcium salt and aging temperature were changedvariously, thereby producing Mg—Al-based hydrotalcite-type particles. InComparative Example 7, the Mg—Al-based hydrotalcite particles wereproduced using an autoclave.

The production conditions are shown in Table 1, and properties of theobtained Mg—Al-based hydrotalcite-type particles are shown in Table 2.

Example 9

1.5 liters of a suspension containing the same Mg—Al-based hydrotalciteparticles as obtained in Example 1 (concentration: 56.7 g/liter) washeated to 70° C., and 8.9 g of water glass #3 was gradually added to thesuspension. After completion of the addition, the obtained mixture wasaged for 60 minutes. The aged mixture was filtered out, washed withwater, dried and then pulverized, thereby obtaining Mg—Al-basedhydrotalcite-type particles surface-coated with hydroxides of silicon.

500 g of the obtained coated hydrotalcite-type particles and 15 g ofnatural rosin were charged into a Henschel mixer, and mixed therein for5 minutes, thereby obtaining Mg—Al-based hydrotalcite-type particlessuccessively surface-coated with hydroxides of silicon and further withthe natural rosin.

Example 10

The Mg—Al-based hydrotalcite-type particles surface-coated withhydroxides of silicon were produced under the same conditions as definedin Example 9.500 g of the obtained coated Mg—Al-based hydrotalcite-typeparticles and 2.5 g of decyltrimethoxy silane were charged into aHenschel mixer, and mixed therein for 5 minutes, thereby obtainingMg—Al-based hydrotalcite-type particles successively surface-coated withhydroxides of silicon and further with decyltrimethoxy silane.

Examples 11 to 15 and Comparative Examples 8 to 11

The same procedures as defined in Examples 9 and 10 were conductedexcept that kind and amount of surface-treating agents added werechanged variously, thereby producing Mg—Al-based hydrotalcite particlessurface-coated with various surface-treating agents. In ComparativeExample 11, the Mg—Al-based hydrotalcite-type particles were producedusing an autoclave.

The particles obtained in Comparative Example 12 were commerciallyavailable Mg—Al-based hydrotalcite-type particles having a plate surfacediameter of 0.25 μm, a thickness of 0.0610 μm, a plate ratio of 4.1 anda specific surface area of 9.2 m²/g ALCAMIZER-1 (tradename)(Mg₄.Al₂(OH)₁₂CO₃.3H₂O) produced by Kyowa Kagaku Kogyo Co., Ltd.) (usedin Example 5 of Japanese Patent Application Laid-Open (KOKAI) No.8-73687(1996)).

The production conditions are shown in Table 3, and properties of theobtained Mg—Al-based hydrotalcite particles are shown in Table 4.

Example 16

The hydrotalcite-type particles obtained in Example 1 and additives weremixed with a vinyl chloride resin at the mixing ratio as shown below. 50g of the resultant mixture was kneaded together at 160° C. for 3 minutesusing a hot roll whose gap was set to 0.75 mm, thereby obtaining akneaded sheet.

Composition Kneaded:

Hydrotalcite-type particles 4.6 parts by weight Vinyl chloride resin(Degree 100 parts by weight of polymerization: 1,300, tradename:Kanebeer, produced by Kanegafuchi Kagaku Co., Ltd.) Trioctyl trimelitate48 parts by weight Zinc stearate (extra pure reagent) 0.8 part by weightStearic acid (extra pure reagent) 0.4 part by weight Dibenzoylmethane0.2 part by weight Dipentaerythritol 0.2 part by weight Calcium stearate(extra 0.1 parts by weight pure reagent) Diethyl phosphite (extra 0.5part by weight pure reagent) (anitioxidants) Calcium carbonate (extra 16parts by weight pure reagent) Antimony trioxide (extra 5 parts by weightpure reagent) Acrylonitrile-styrene copolymer 2 parts by weight (gellingaccelerators)

The thus obtained kneaded sheet was pressure-treated using a hot press,thereby preparing a sheet piece having a thickness of 1.5 mm. The pressconditions were as follows:

-   -   press temperature: 160° C.; press pressure: 100 kg/cm²;    -   press time: 1 minute; press gap: 1.0 mm; and    -   amount treated: 35 g.

The heat stability of the obtained sheet piece was 511 minutes. The rankof the heat discoloration resistance thereof was “A”. The electricinsulating property thereof was 12.8×10¹³ Ω·cm.

Examples 17 to 27 and Comparative Examples 13 to 19

The same procedures as defined in Example 16 were conducted except thatthe Mg—Al-based hydrotalcite-type particles obtained in Examples 1 and 9to 16 and Comparative Examples 1 and 8 to 12, the amount of zincstearate added, the amount of calcium stearate added and the amount ofdipentaerythritol added, were changed variously, thereby preparing avinyl chloride resin composition. The blended components and evaluationresults of the obtained resin composition are shown in Table 5.

Example 28

The same procedures as defined in Example 16 were conducted except thatthe hydrotalcite-type particles obtained in Example 9 and additives weremixed with a vinyl chloride resin at the mixing ratio as shown below,thereby obtaining a kneaded sheet.

Composition Kneaded:

Hydrotalcite-type particles 3.5 parts by weight Vinyl chloride resin(Degree 100 parts by weight of polymerization: 1,300, tradename:Kanebeer, produced by Kanegafuchi Kagaku Co., Ltd.) Diisononyl phthalate50 parts by weight Zinc stearate (extra pure reagent) 1.2 part by weightDibenzoylmethane 0.2 part by weight Diethyl phosphite (extra 0.2 part byweight pure reagent) (anitioxidants) Clay 0 part by weight Calciumcarbonate (extra 16 parts by weight pure reagent)

Examples 29 to 33 and Comparative Example 20

The same procedures as defined in Example 28 were conducted except thatthe Mg—Al-based hydrotalcite-type particles obtained in Examples 9 and10, the amount of zinc stearate added, the amount of clay added and theamount of calcium carbonate added, were changed variously, therebypreparing a vinyl chloride resin composition. The blended components andevaluation results of the obtained resin composition are shown in Table6.

TABLE 1 Production of Mg-Al-based hydrotalcite-type particles Amount ofExamples and reaction Mg compound Comparative solution ConcentrationExamples (liter) Kind (mol/liter) Example 2 5.0 MgSO₄ 0.375 Example 35.0 MgSO₄ 0.375 Example 4 5.0 MgSO₄ 0.375 Example 5 5.0 MgSO₄ 0.375Example 6 5.0 MgSO₄ 0.400 Example 7 5.0 MgSO₄ 0.250 Example 8 5.0 MgCl₂0.375 Comparative 5.0 MgSO₄ 0.375 Example 1 Comparative 5.0 MgSO₄ 0.375Example 2 Comparative 5.0 MgSO₄ 0.375 Example 3 Comparative 5.0 MgSO₄0.375 Example 4 Comparative 5.0 MgSO₄ 0.375 Example 5 Comparative 5.0MgSO₄ 0.375 Example 6 Comparative 5.0 MgSO₄ 0.375 Example 7 Productionof Mg-Al-based hydrotalcite-type particles Examples and Al compoundConcentration Comparative Concentration of Na₂CO₃ Examples Kind(mol/liter) (mol/liter) Example 2 Al₂(SO₄)₃ 0.0625 0.0875 Example 3Al₂(SO₄)₃ 0.0625 0.0875 Example 4 Al₂(SO₄)₃ 0.0625 0.0875 Example 5Al₂(SO₄)₃ 0.0625 0.0875 Example 6 Al₂(SO₄)₃ 0.050 0.0700 Example 7Al₂(SO₄)₃ 0.125 0.1750 Example 8 AlCl₃ 0.125 0.0875 ComparativeAl₂(SO₄)₃ 0.0625 0.0875 Example 1 Comparative Al₂(SO₄)₃ 0.0625 0.0875Example 2 Comparative Al₂(SO₄)₃ 0.0625 0.0875 Example 3 ComparativeAl₂(SO₄)₃ 0.0625 0.0875 Example 4 Comparative Al₂(SO₄)₃ 0.0625 0.0875Example 5 Comparative Al₂(SO₄)₃ 0.0625 0.0875 Example 6 ComparativeAl₂(SO₄)₃ 0.0625 0.0875 Example 7 Production of Mg-Al-basedhydrotalcite-type particles Amount of Ca Examples and Concentrationadded Concentration Comparative of NaOH Ca/(Mg + Al) of Ca Examples(mol/liter) (molar ratio) (mol/liter) Example 2 2.685 0.06 0.03 Example3 3.205 0.06 0.03 Example 4 3.135 0.02 0.01 Example 5 3.325 0.136 0.068Example 6 3.185 0.06 0.03 Example 7 3.185 0.06 0.03 Example 8 3.185 0.060.03 Comparative 3.185 0.06 0.03 Example 1 Comparative 3.125 0 0 Example2 Comparative 3.130 0.005 0.0025 Example 3 Comparative 3.355 0.23 0.115Example 4 Comparative 3.185 0.06 0.03 Example 5 Comparative 1.285 0.060.03 Example 6 Comparative 3.125 0 0 Example 7 Production of Mg-Al-basedhydrotalcite-type particles Examples pH value of and Aging suspensionAging Comparative Addition method temperature during time Examples of Ca(° C.) aging (−) (hr) Example 2 Charged after 80 11.2 3 adding Mg and AlExample 3 Charged after 95 12.3 18 adding Mg and Al Example 4 Chargedafter 95 12.4 18 adding Mg and Al Example 5 Charged after 95 12.0 18adding Mg and Al Example 6 Charged after 95 12.2 18 adding Mg and AlExample 7 Charged after 95 11.9 18 adding Mg and Al Example 8 Charged 9512.5 18 simultaneously with addition of Mg and Al Comparative Notcharged 95 12.3 18 Example 1 Comparative Charged after 95 12.2 18Example 2 adding Mg and Al Comparative Charged after 95 12.0 18 Example3 adding Mg and Al Comparative Charged after 95 12.3 18 Example 4 addingMg and Al Comparative Charged after 50 12.2 18 Example 5 adding Mg andAl Comparative Charged after 95 8.8 18 Example 6 adding Mg and AlComparative Not charged 150 12.0 18 Example 7

TABLE 2 Properties of Mg-Al-based hydrotalcite-type particles ExamplesPlate Specific and surface surface Comparative diameter Thickness Plateratio area Examples (μm) (μm) (−) (m²/g) Example 2 0.20 0.0337 5.9 38.6Example 3 0.80 0.0645 12.4 10.2 Example 4 0.25 0.0530 4.7 14.8 Example 50.21 0.0425 4.9 35.4 Example 6 0.23 0.0325 7.1 37.7 Example 7 0.220.0280 7.9 59.2 Example 8 0.41 0.0611 6.7 12.0 Comparative 0.08 0.01006.0 95.2 Example 1 Comparative 0.07 0.0125 5.6 85.5 Example 2Comparative 0.05 0.0138 3.6 100.8 Example 3 Comparative 0.09 0.0202 4.580.6 Example 4 Comparative 0.07 0.0155 4.5 116.8 Example 5 Comparative0.06 0.0180 3.3 86.5 Example 6 Comparative 0.40 0.0616 6.5 10.6 Example7 Properties of Mg-Al-based hydrotalcite-type Examples particles andComposition: Comparative Crystal [Mg_(x)Ca_(y)].Al_(z).(OH)₂.A^(n−)_(p).mH₂O Examples structure x y z Example 2 Hydrotalcite- 0.706 0.0520.242 type Example 3 Hydrotalcite- 0.702 0.058 0.240 type Example 4Hydrotalcite- 0.740 0.020 0.240 type Example 5 Hydrotalcite- 0.658 0.1200.222 type Example 6 Hydrotalcite- 0.755 0.056 0.189 type Example 7Hydrotalcite- 0.470 0.056 0.474 type Example 8 Hydrotalcite- 0.708 0.0550.237 type Comparative Hydrotalcite- 0.708 0.054 0.238 Example 1 typeComparative Hydrotalcite- 0.745 0 0.255 Example 2 type ComparativeHydrotalcite- 0.742 0.005 0.253 Example 3 type Comparative Hydrotalcite-0.612 0.185 0.203 Example 4 type Comparative Hydrotalcite- 0.708 0.0540.238 Example 5 type Comparative Hydrotalcite- 0.708 0.054 0.238 Example6 type Comparative Hydrotalcite- 0.752 0 0.248 Example 7 type Propertiesof Mg-Al-based hydrotalcite-type particles Examples Heat-resisting andCa Al Carbon time of kneaded Comparative content content content vinylchloride Examples y/(x + z) z/(x + z) (wt. %) sheet (hr) Example 2 0.0550.255 2.056 5 Example 3 0.062 0.255 2.155 6 Example 4 0.020 0.245 2.0115 Example 5 0.136 0.252 2.168 5 Example 6 0.059 0.200 2.003 6 Example 70.059 0.502 2.111 5 Example 8 0.058 0.251 2.002 5 Comparative 0.0570.252 2.122 3 Example 1 Comparative 0 0.255 2.148 2 Example 2Comparative 0.005 0.254 2.024 3 Example 3 Comparative 0.227 0.249 2.1853 Example 4 Comparative 0.057 0.252 2.047 2 Example 5 Comparative 0.0570.252 2.088 2 Example 6 Comparative 0 0.248 2.155 3 Example 7

TABLE 3 Production of Mg-Al-based hydrotalcite-type particles Amount ofExamples and reaction Mg compound Comparative solution ConcentrationExamples (liter) Kind (mol/liter) Example 9 5.0 MgSO₄ 0.375 Example 105.0 MgSO₄ 0.375 Example 11 5.0 MgSO₄ 0.375 Example 12 5.0 MgSO₄ 0.375Example 13 5.0 MgSO₄ 0.250 Example 14 5.0 MgSO₄ 0.250 Example 15 5.0MgSO₄ 0.250 Comparative 5.0 MgSO₄ 0.375 Example 8 Comparative 5.0 MgSO₄0.375 Example 9 Comparative 5.0 MgSO₄ 0.375 Example 10 Comparative 5.0MgSO₄ 0.375 Example 11 Production of Mg-Al-based hydrotalcite-typeparticles Examples and Al compound Concentration ComparativeConcentration of Na₂CO₃ Examples Kind (mol/liter) (mol/liter) Example 9Al₂(SO₄)₃ 0.0625 0.0875 Example 10 Al₂(SO₄)₃ 0.0625 0.0875 Example 11Al₂(SO₄)₃ 0.0625 0.0875 Example 12 Al₂(SO₄)₃ 0.0625 0.0875 Example 13Al₂(SO₄)₃ 0.0625 0.0875 Example 14 Al₂(SO₄)₃ 0.0625 0.0875 Example 15Al₂(SO₄)₃ 0.125 0.1750 Comparative Al₂(SO₄)₃ 0.0625 0.0875 Example 8Comparative Al₂(SO₄)₃ 0.0625 0.0875 Example 9 Comparative Al2(SO4)30.0625 0.0875 Example 10 Comparative Al2(SO4)3 0.0625 0.0875 Example 11Production of Mg-Al-based hydrotalcite-type particles Amount of CaExamples and Concentration added Concentration Comparative of NaOHCa/(Mg + Al) of Ca Examples (mol/liter) (molar ratio) (mol/liter)Example 9 3.185 0.06 0.03 Example 10 3.185 0.06 0.03 Example 11 2.6850.06 0.03 Example 12 3.205 0.08 0.04 Example 13 3.135 0.02 0.01 Example14 3.325 0.136 0.068 Example 15 3.185 0.06 0.03 Comparative 3.130 0.0050.0025 Example 8 Comparative 3.355 0.23 0.115 Example 9 Comparative3.185 0.06 0.03 Example 10 Comparative 3.125 0 0 Example 11 Productionof Mg-Al-based hydrotalcite-type particles Examples pH value of andAging suspension Aging Comparative Addition method temperature duringtime Examples of Ca (_C.) aging (−) (hr) Example 9 Charged after 95 12.518 adding Mg and Al Example 10 Charged after 95 12.5 18 adding Mg and AlExample 11 Charged after 80 11.2 3 adding Mg and Al Example 12 Chargedafter 95 12.3 18 adding Mg and Al Example 13 Charged after 95 12.4 18adding Mg and Al Example 14 Charged after 95 12.0 18 adding Mg and AlExample 15 Charged after 95 11.9 18 adding Mg and Al Comparative Chargedafter 95 12.0 18 Example 8 adding Mg and Al Comparative Charged after 9512.3 18 Example 9 adding Mg and Al Comparative Charged after 50 12.2 18Example 10 adding Mg and Al Comparative Not charged 150 12.0 18 Example11 Production of Mg-Al-based hydrotalcite-type particlesSurface-treatment Amount added based Examples on the weight of andhydrotalcite-type Comparative particles Examples Kind (wt. %) Example 9Water glass #3/natural rosin 3.0/3.0 Example 10 Water glass #3/ 3.0/0.5decyltrimethoxy silane Example 11 Water glass #3/ 3.0/1.5decyltrimethoxy silane Example 12 Water glass #3/natural rosin 3.0/3.0Example 13 Water glass #3/natural rosin 3.0/3.0 Example 14 Water glass#3/ 3.0/1.5 decyltrimethoxy silane Example 15 Natural rosin 5.0Comparative Water glass #3/natural 3.0/6.0 Example 8 rosin ComparativeWater glass #3/ 3.0/8.0 Example 9 decyltrimethoxy silane ComparativeWater glass #3/Natural 3.0/6.0 Example 10 rosin Comparative Water glass#3/natural 3.0/3.0 Example 11 rosin

TABLE 4 Properties of Mg—Al-based hydrotalcite-type particles Heat-Exam- resisting ples Silicon time of and content kneaded Compar- PlateSpecific (calcu- vinyl ative surface Thick- Plate surface CrystalComposition: Ca Al lated as Carbon chloride Exam- diameter ness ratioarea struc- [MgxCay].Alz.(OH)2.An-p.mH2O content content SiO2) contentsheet ples (μm) (μm) (−) (m2/g) ture x y z y/(x + z) z/(x + z) (wt. %)(wt. %) (hr) Exam- 0.40 0.0605 6.7 10.8 Hydro- 0.709 0.055 0.236 0.0580.250 0.11 3.227 6 ple 9 talcite- type Exam- 0.40 0.0605 6.7 11.1 Hydro-0.709 0.055 0.236 0.058 0.250 0.13 3.156 6 ple 10 talcite- type Exam-0.20 0.0337 5.9 33.6 Hydro- 0.706 0.052 0.242 0.055 0.255 0.14 3.392 5ple 11 talcite- type Exam- 0.80 0.0645 12.4 10.1 Hydro- 0.702 0.0580.240 0.062 0.255 0.12 3.099 6 ple 12 talcite- type Exam- 0.25 0.05304.7 13.8 Hydro- 0.740 0.020 0.240 0.020 0.245 0.11 3.148 6 ple 13talcite- type Exam- 0.21 0.0425 4.9 32.8 Hydro- 0.658 0.120 0.222 0.1360.252 0.13 3.888 5 ple 14 talcite- type Exam- 0.22 0.0280 7.9 55.5Hydro- 0.470 0.056 0.474 0.059 0.200 — 3.477 6 ple 15 talcite- typeCompar- 0.05 0.0138 3.6 93.5 Hydro- 0.742 0.005 0.253 0.005 0.254 0.113.738 3 ative talcite- Exam- type ple 8 Compar- 0.09 0.0202 4.5 72.8Hydro- 0.612 0.185 0.203 0.227 0.249 0.14 3.888 3 ative talcite- Exam-type ple 9 Compar- 0.07 0.0155 4.5 109.1 Hydro- 0.708 0.054 0.238 0.0570.252 0.12 3.672 2 ative talcite- Exam- type ple 10 Compar- 0.40 0.06166.5 10.5 Hydro- 0.752 0 0.248 0 0.248 0.13 3.338 3 ative talcite- Exam-type ple 11 Compar- 0.25 0.0610 4.1 9.2 Hydro- 0.678 0 0.322 0 0.4750.11 3.521 3 ative talcite- Exam- type ple 12

TABLE 5 Examples Kind of Composition (wt. part) and hydrotalcite- VinylHydrotalcite- Comparative type chloride type Zinc Examples particlesresin particles stearate Example 16 Example 1 100 4.6 0.8 Example 17Example 9 100 4.6 0.8 Example 18 Example 10 100 4.6 0.8 Example 19Example 11 100 4.6 0.8 Example 20 Example 12 100 4.6 0.8 Example 21Example 13 100 4.6 0.8 Example 22 Example 14 100 4.6 0.8 Example 23Example 15 100 4.6 0.8 Example 24 Example 10 100 4.6 2.0 Example 25Example 9 100 4.6 0.5 Example 26 Example 10 100 4.6 1.2 Example 27Example 9 100 4.6 1.2 Comparative Comparative 100 4.6 0.8 Example 13Example 1 Comparative Comparative 100 4.6 0.8 Example 14 Example 8Comparative Comparative 100 4.6 0.8 Example 15 Example 9 ComparativeComparative 100 4.6 0.8 Example 16 Example 10 Comparative Comparative100 4.6 0.8 Example 17 Example 11 Comparative Comparative 100 4.6 0.8Example 18 Example 12 Comparative Example 11 100 1.0 0.8 Example 19Examples and Composition Comparative (wt. part) ExamplesDipentaerythritol Calcium stearate Example 16 0.2 0.1 Example 17 0 0.1Example 18 0.2 0.1 Example 19 0.4 0 Example 20 0 0 Example 21 0 0.1Example 22 0.2 0 Example 23 0.4 0.1 Example 24 0 0 Example 25 0 0.1Example 26 0 0 Example 27 0 0 Comparative 0.2 0.1 Example 13 Comparative0.4 0.1 Example 14 Comparative 0.2 0 Example 15 Comparative 0.4 0.1Example 16 Comparative 0 0 Example 17 Comparative 0 0 Example 18Comparative 0 0 Example 19 Examples Evaluation results and VolumeComparative Heat stability Coloring resistivity Examples (min.) property(_ 1013 (.cm) Example 16 511 A 12.8 Example 17 601 A 45.5 Example 18 588A 30.5 Example 19 469 A 16.1 Example 20 590 A 24.8 Example 21 599 A 28.3Example 22 522 A 18.1 Example 23 432 A 13.2 Example 24 956 A 22.2Example 25 519 A 38.8 Example 26 700 A 25.5 Example 27 862 A 30.8Comparative 165 C 1.9 Example 13 Comparative 132 D 2.4 Example 14Comparative 170 C 2.3 Example 15 Comparative 112 D 1.8 Example 16Comparative 250 B 2.8 Example 17 Comparative 214 C 2.4 Example 18Comparative 82 C 1.8 Example 19

TABLE 6 Examples Kind of Composition (wt. part) and hydrotalcite- VinylHydrotalcite- Comparative type chloride type Zinc Examples particlesresin particles stearate Example 28 Example 9 100 3.5 1.2 Example 29Example 9 100 3.5 1.4 Example 30 Example 10 100 3.5 2.0 Example 31Example 9 100 3.5 0.8 Example 32 Example 9 100 3.5 1.0 Example 33Example 10 100 3.5 1.2 Comparative Example 9 100 1.0 0.8 Example 20Examples and Comparative Blended components Examples Clay CaCO₃ Example28 0 16 Example 29 0 16 Example 30 0 16 Example 31 10 20 Example 32 1020 Example 33 10 20 Comparative 0 16 Example 20 Evaluation resultsExamples and Volume Comparative Heat stability Coloring resistivityExamples (min.) property (× 10¹³ Ω · cm) Example 28 420 A 18.2 Example29 603 A 25.1 Example 30 707 A 20.1 Example 31 759 A 33.3 Example 32 821A 40.5 Example 33 719 A 36.6 Comparative 116 C 2.6 Example 20

1. A chlorine-containing resin composition for covering an electricwire, having a heat stability of not less than 240 minutes and a volumeresistivity of 5.0×10¹³ to 1.0×10¹⁶ Ω cm when measured according to JISK6723, and comprising: 100 parts by weight of a chlorine-containingresin, and 1.5 to 10 parts by weight of Mg—Al-based hydrotalciteparticles having a composition represented by the formula:[Mg_(x)Ca_(y)].Al_(z).(OH)₂.A^(n−) _(p).mH₂O wherein 0.2≦z/(x+z)≦0.6;0.01≦y/(x+z)≦0.20; x+y+z=1; p=(2(x+y−1)+3z)/n; A is a n-valent anion;and m is more than 0 and not more than 0.75, having a plate surfacediameter of 0.1 to 1.0 μm and a thickness of 0.02 to 0.08 μm, andcontaining calcium at a molar ratio of Ca to a sum of Mg and Al of0.01:1 to 0.20:1, and showing a heat-resisting time of not less than 4hours.
 2. A chlorine-containing resin composition according to claim 1,wherein the ratio: z/(x+z) wherein x is Mg and z is Al, is 0.2:1 to0.6:1.
 3. A chlorine-containing resin composition according to claim 1,wherein said anion A^(n−)is selected from the group consisting of ahydroxy ion (OH⁻), a carbonate ion (CO₃ ²⁻) and a sulfate ion (SO₄ ²⁻).4. A chlorine-containing resin composition according to claim 1, whichfurther contains a plasticizer in an amount of 30 to 90 parts by weightbased on 100 parts by weight of the chlorine-containing resin.
 5. Achlorine-containing resin composition according to claim 1, whichfurther contains a zinc compound in an amount of 0.2 to 2.5 parts byweight based on 100 parts by weight of the chlorine-containing resin.